STYLE 2002 - TEADIT

STYLE 2002Carbon Yarn, Graphite Filled

Description and Applications

Service Limits

Temperature ºF (ºC)

Minimum -400 (-240)

Maximum 842 (450)

Steam 1202 (650)

Pressure psi (bar)

Static 4351 (300)

Rotating 362 (25)

Reciprocating 1450 (100)

pH

Minimum 0

Maximum 14

Shaft Speed f/m (m/s)

Maximum 3937 (20)

Temperature ºF (ºC)
Minimum	-400 (-240)
Maximum	842 (450)
Steam	1202 (650)

Pressure psi (bar)
Static	4351 (300)
Rotating	362 (25)
Reciprocating	1450 (100)

pH
Minimum	0
Maximum	14

Shaft Speed f/m (m/s)
Maximum	3937 (20)

Approximate Yields (+/-10%)

Size

Ft/Lb

88.9

43.2

27.5

16.6

8.7

6.9

5.2

4.5

3.3

2.3

1.7

Inch

1/8

3/16

1/4

5/16

3/8

7/16

1/2

9/16

5/8

3/4

7/8

Package

1 Lb (0.5kg)

2 Lbs (1kg)

5 Lbs (2kg)

10 Lbs (5kg)

Other spools are availabel on request

Datasheet STYLE 2002
Teadit® 2002 - Paper Refiner

See also in Echelon-HF ™

Compression packings Compressed Fiber Sheets Metallic Gaskets PTFE Products ePTFE Products Flexible Graphite Products NSF-61 Products FDA Compliant Products High Temperature Products Teadit Origin™ Technology Low Emissions Family

Developing A Special Camprofile Gasket For a Pressure Vessel

Style 2007 in Chemical Slurry

A chemical processing facility was having issues maintaining adequate sealing on a slurry pump with their existing packing, requiring retightening every few hours.

Thermic Fluid Case History

Dual Packing Combination Kit in Sugar Industry

2774 and Sealpak® 46

2235 in Steam Application Case History

A chemical processing facility was experiencing steam leakage on a sulphonator vessel after only a couple of weeks of run-time leading to reduced efficiency in the process and longer required run times.

Teadit 24SH in Chemical Processing

A chemical processing facility was experiencing leaks on FRP flange connections due to damage to the flanges caused by the use of gaskets that were not suitable for the requirements of low strength flanges, like FRP.

Teadit Camprofile Gasket in Chemical Processing

A PTFE manufacturing facility was experiencing leaks on an FEP Extruder that was originally designed to utilize a metal reinforced compressed asbestos gasket.

ETP Copper Process Case History

A metal manufacturer was looking for a replacement for asbestos compression packing.

CMS Plant Case History

A chemical plant was having issues with skived virgin PTFE gaskets failing in a heat exchanger application.

2774 Harsh Chemicals Case History

A customer was using a PTFE packing from another manufacture in an auger conveyor system.

Teadit Distributors

STYLE 2002Carbon Yarn, Graphite Filled

Datasheet STYLE 2002

Teadit® 2002 - Paper Refiner

See also in Echelon-HF ™